Stablity: Stable, but breaks down slowly in uv light or sunlight. Incompatible with halogens, strong oxidizing agents, benzene, petroleum ether, aromatic and chlorinated hydrocarbons, lubricating oils.
1. Products properties
High density polyethylene for non-toxic, tasteless, no smelly white particles, melting point is about 130 ° C, relative density of 0.941 ~ 0.960. It has good heat resistance and cold resistance, chemical stability, but also has high rigidity and toughness, good mechanical strength. Dielectric properties, environmental stress cracking resistance sex also is good.
Make barrela, plastic bottle and bag, make all kind of pipes, make shading net, and make cable wire-insulating
Shelf life: It should avoid damp, contaminated and direct sun light during transport. And should be stored in ventilated and dry place. Do not put it with flammable and corrosive substances together, and away from the fire.
|HDPE cable material Property||Typical Value|
|Mass density g/cm 3||0.941-0.959|
|Melt flow Rate(190 centidegree /2.16kg)g/10min||≤1.0|
|Tensile yield strength MPa||≥19.0|
|Flexural modulus Mpa||≥965|
|Elongation@ break %||≥400|
|Impact Embrittlement temperature centidegree||MAX -118|
|Loss Tangent||100KHZ||MAX 0.0001|
|Volume resistivity OHM-CM||MIN 1x10 15|
2. Blow Molding HDPE Grades
|Melt Temperature||180 to 220 °C|
|Melt flow rate (MFR)||0.4 g/10 min (190°C/2.16kg)|
|Melt flow rate (MFR)||30 g/10 min (190°C/21.6kg)|
|Melt flow rate (MFR)||1.5 g/10 min (190°C/5.0kg)|
|Tensile Modulus||1000 MPa|
|Tensile Stress at Yield||23.0 MPa|
|Tensile Strain at Yield||10 %|
|Charpy notched impact strength||5.5 kJ/m² (-30 °C)|
|Charpy notched impact strength||12.0 kJ/m² (23 °C)|
|Vicat softening temperature||70 °C (B50 (50°C/h 50N))|
|Shore hardness||60 (Shore D)|
|Ball indentation hardness||44 MPa (H 132/30)|
|ESCR (Basell)||65 hr|